Good deal . How long did ya cook them ?
thanks
animal
On 4/27/24 8:45 PM, Mike Poore wrote:
toggle quoted message
Show quoted text
Just an update in case anyone is interested. I annealed the tool
holders at 1550 F. Before annealing, they tested at 45 HRC. After
annealing, they tested at 8 HRC. I have read I should use a B
scale tester, but I do not have one. A scrap piece of 1018 tested
at 15 HRC, so these holders should be easy milling.
On 4/25/2024 11:37 AM, Mike Poore via
groups.io wrote:
I did a search for that number. The indicates that is the Swedish
equivalent to 4340.
Sorry for wasting everyone's time. I hate when people ask easily
answered questions and I am guilty. I found this that lists the HT specs
for most alloys. 1550F is within the annealing range of almost
every alloy on the list. 1500F is within the hardening range for
almost all alloys. I will have to do more research on tempering,
but for an insert holder there should be a wide tolerance.
On 4/25/2024 1:17 AM, Andrei via
groups.io wrote:
Found a reference online to SS2541 being used
for tool bit holders. Maybe check that.?
The problem is I do not know the alloy. I guess I will
use the 4140 specs.
On 4/25/2024 12:59 AM, Andrei
via groups.io wrote:
That is definitely a great option. I don't
have one so my go-to was carbide and coolant.youbare in
great shape with the oven
I have a heat treating oven right next to my mill, so
I would rather use the oven.
On 4/24/2024 11:02 PM,
Andrei via groups.io wrote:
Are short of squirter bottles or
endmills?
Not an option for me.
On 4/24/2024 9:43
PM, Andrei via groups.io wrote:
Use a carbide endmill and coolant.
No need to anneal
Anyone happen to know the alloy most likely
to be used for carbide insert tool holders? My
guess is 4140. I have four that I need to mill
down to work in an AXA holder. They test at 45
HRC. Thinking about annealing them before
milling and then heat treating again, so I would
like specs to use.